Beige - Sandstone
Quarry Location: Amherst, Cleveland, Ohio
Water Absorption: 6.2 %
Density: 2119 Kg/m3
Flexural Strength: 5.28 MPa
Compressive Strength: 70.1 MPa
Recommended Usage: Monuments, building stone, ornamental stone, stairs, interior, exterior wall and floor applications, mosaic, waterjet pattern, wall panels, table tops, window sills, wall and pool copings, pool pavers, sculptures, cobbles, pavers, curbstone
Finishing Surface: Flamed,Bush Hammered,Tumbled,Brushed,Honed,Split,Machine Cut,Natural Surface,Sandblasted,Acid Washing,Combed,Water Jet,Filled,Chiseled,Pickling
Additional Names: Ohio Sandstone, Amherst Sandstone,Berea Sandstone
Berea Sandstone is a natural stone with a distinctive and earthy appearance, hailing from the region of Amherst, Cleveland, Ohio. Here are some key features of this sandstone:
Color Palette: Berea Sandstone is characterized by its fine-grained texture, which gives it a smooth and consistent appearance. The primary color is a dark beige with intriguing brown speckles, creating a sense of depth and character. Additionally, earthy gray hues are interwoven into the stone's composition, adding further visual interest.
Origin: This sandstone is quarried in Amherst, Cleveland, Ohio. The Amherst region is renowned for its production of high-quality sandstone, making Berea Sandstone a sought-after choice for various applications.
Berea Sandstone is a versatile and durable material that lends itself well to a variety of construction and design uses, such as building facades, flooring, and even decorative elements. Its fine-grained texture, unique coloration, and durability make it a valuable and popular resource in the realm of natural stone.
ASTM C170 Compressive Strength PSI 70.1 MPa
ASTM C-99 Modules of Rupture 5.28 MPa
ASTMC-97 Absorption and Bulk Specific Gravity
Absorption Bulk Specific Gravity
6.2 % -- 2119 Kg/m3
ASTM C-241Abrasion Resistance of Stone Subjected to Foot Traffic
Abrasive Hardness Value (1.1a) 9.48
Berea Sandstone Facts
Silica (SiO2): 93.13%
Alumina (A12O3): 3.86%
Ferric Oxide (Fe2O3): 0.11%
Ferrous Oxide (FeO): 0.54%
Magnesium Oxide (MgO): 0.25%
Calcium Oxide (CaO): 0.10%
Alkali: Alk
Loss on Ignition: 1.43%