COMPOSITION COMPONENT A: Thixotropized epoxy resin (molecular weight >700) with fillers and pigments, COMPONENT B: Mixture of cycloaliphatic amine, polyamide and tertiary thixotropized amine fed catalyzing agents with fillers and pigments USE Permanent bonding of granite , marble, natural stones between them or with other supports (metals, terracotta, concrete, etc.)
MIXING RATIO Epoxy adhesives require exact mixing ratio, in weight, between component A (resin) and component B (catalyst). In the particular case the ratio is: COMPONENT A : COMPONENT B = 100 : 100 (i.e.: 100 gr. of component A mixed with 100 gr. of component B) SURFACE PREPARATION Surface to be treated/glued to be porous, clean, dry and free from dust, grease or any other extraneous substances.
MIXING Mix the components as indicated in MIXING RATIO section until completely blended. The two components (A+B) must be carefully mixed to obtain catalytic homogeneity
PACKAGING set A+B of 250 ml. or 1 L. or 2 L. (3 kg.) - set A+B of 10 kg. or 20 kg.
APPLICATION With putty knife or spreading. Do not apply at temperature lower than +10°C (50°F) Suggested temperature of application between +10°C / 50°F and +30°C / 86°F
THICKNESS Recommended 0,2 to 1 mm CONSUMPTION 250 to 700 gr/m²
POLYMERISATION The rate of reaction increases with the temperature, which should never be lower than +10°C (50°F)
HARDENING 6 to 12 hours according to environmental conditions (temperature, humidity, etc.). Catalysis completed after 24 hours.
TECHNICAL DATA see page 2
NOTE Based on data reported, workability time is considered to be 30 to 35 minutes Do not store at temperature lower than +10°C (50°F) and higher than +35°C(95°F). Protect from frost the stored cans/tins
SHRINKAGE 0,3% abt.