Item Details
Quarry Location:
Tivoli Terme (Rome)
Water Absorption:
0.58 %
Density:
2517 Kg/m³
Flexural Strength:
10.71-11.67 MPa
Compressive Strength:
68.39-73.22 MPa
Recommended Usage:
Building stone, sinks, monuments, pool coping, sills, ornamental stone, interior, exterior, wall, floor , paving
Finishing Surface:
Honed, Aged, Polished, Sawn Cut, Sanded, Rockfaced, Sandblasted, Bushhammered, Tumbled
Additional Names:
Roman Travertine Silver Mic,Travertino Silver, Travertino Romano Silver Mic,Travertino Silver Mic
Description:
Physical - Mechanical Characteristic ( ASTM STANDARD)
Apparent Specific Weight - C97 - 2517 Kg/m3
Absorption Coefficient - C97 - 058%
Compressive Strenght Dry - C170 - 73,22 Mpa/Mpa
Compressive Strenght Wet - C170 - 68,39 Mpa/Mpa
Modulus of Rupture Dry - C99 - 10,71 Mpa/Mpa
Modulus of Rupture Wet - C99 - 11,67 Mpa/Mpa
Flexural Strenght Dry - C880 - 10,21 Mpa/Mpa
Flexural Strenght Wet - C880 - 11,60 Mpa/Mpa
Resistance to Abrasion - C241 - 14,65 Mpa/Mpa
Static Coefficient Of Friction Dry - C1028 - 0,60 Mpa/Mpa
Static Coefficient Of Friction Wet - C1028 - 0,57Mpa/Mpa
Chemical Composition:
Apparent and Insoluble Silicons in Hydrochloric Acid - 0,012
Soluble Silicon Acid, Calculeted as Qnhhydride - 0,636
CO2 - 43,495
SO3 - 0,230
P2O5 - 0,017
A12O3 - 0,170
Fe2O3 - 0,031
FeO - 0,016
CaO - 54,712
MgO - 0,541
Other Indeterminates and Losses 0,140
Specific Weight 2,457