Pure White Nano Crystallized Glass Stone Slabs/Glass Stone Tiles & Slabs

2. Origin

China

3. Stone Form

Customized paquet

4. Size

Customized

Both large size and cut-to-size tiles can be provided.

Large size: 900mm *2500 mm

Cut-to-size: 900*900, 800*800, 600*600, 300*600, 300*300

5. Thickness

7mm~17mm

6. Color

Available color: Ivory, Beige & Coffee,Black ,Red

7.Certification

CE, SGS, ISO9001, ISO14001, CTC, etc

8. Usage

Industria,Residential,Civil,Others

9.Customized

Customized size , Wide range of different processed products.

No.

Test item(s)

Test result(s)

Test method(s)

1

Moh's hardness

grade 6

JC/T872-2000

2

Chemical stability

Acid fastness

k=0.05%

Alkali fastness

k=0.05%

3

Glossiness

99

4

Flexural strength

57.5MPa

5

Radioactivity

IRa

0.2

GB6566-2010

Iγ

0.5

6

Thermal conductivity

1.175W(M·K)

GB/T10297-1998

7

P-T-P resistance

3.79×1010Ω

SJ/T10694-2006

8

Water absorption

0.006%

Refer to GB/T3810.3-2006

9

Stain resistance

Level 5

Refer to GB/T3810.14-2006

10

Freezing resistance

No crack and peeling

Refer to GB/T3810.12-2006

11

Straight bore

-0.17% ~ +0.22%

Refer to GB/T3810.12-2006

12

Surface flatness

Side camber

-0.02% ~ +0.05%

Warpage

-0.06% ~ +0.01%

Center camber

-0.07% ~ +0.01%

13

Wear resistance

Level 4

Refer to GB/T3810.7-2006

14

Moisture expansion

0.02mm/m

Refer to GB/T3810.10-2006

15

CLTE

7.88×10-6ºC-1

Refer to GB/T3810.8-2006

16

Impact resistance

0.78

Refer to GB/T3810.5-2006

17

Absorption by weight

0.02%

ASTM C97/C97M-09

18

Density

2690 kg/m³

19

Abrasion resistance(polished)

46

ASTM C241/C241-013

20

Modulus of rupture

Dry condition: 63.6 Mpa

Refer to ASTM C99/C99-09

Wet condition: 63.6 Mpa

21

Compressive strength

Dry condition: 446 Mpa

Refer to ASTM C170/C170-09

Wet condition: 427 Mpa

22

Static coefficient of friction

Dry condition: 0.84

ASTM C1028-07

Wet condition: 0.50

23

Liner thermal expansion coefficient

5.6×10-6/ºC

ASTM C531-00(2012)