Stone Lamination Epoxy for Marble with Ceramic

Stone lamination epoxy for marble with ceramic

Item No.: 1192

Mix ratio by weight: A:B=2:1

Application: It is mainly used for the composite bonding of marble (beige, orange net, black and white root, wood grain, brilliant gold and blue) with granite or ceramic substrates.

• 

• 1

• 2

• 3

Composite Epoxy

Item No.: 1192

Mix ratio by weight: A:B=2:1

Application: It is mainly used for the composite bonding of marble (beige, orange net, black and white root, wood grain, brilliant gold and blue) with granite or ceramic substrates.

[Features/Advantages]
1. Modified epoxy adhesive with moderate viscosity;
2. easy to brush, curing shrinkage rate is very small;
3. Low stress;
4. high bonding strength;
5. the thermal expansion coefficient is close to the stone, wear-resistant, anti-aging, cold and heat resistant alternating impact, good corrosion resistance;
6. no sag, easy to operate;
7. The coefficient of linear expansion is small, the dimensional stability of the product after curing is good, and the sheet is not deformed;
8. green products

[Scope of application]
It is mainly used for the lamination for marble (Beige, Emperador, bBlack Marquina, GIALLO ATLANTIDE) with granite or ceramic.

【Technical data】

Note: The above is based on mixed glue in 600g

【Steps for usage】
1. The water used for grinding and thickening of the plates should be clean and non-polluting fresh water;
2. The board to be laminated should be free of impurities such as dust, dirt, sand and oil;
3. The board to be laminated must be dry by oven or under natural condition
4. The surface of the composite material must be in flat.
5. Firstly mix the glues of components A and B separately with an electric mixer.
6. Mix the glue according to the specified ratio A:B=2:1 (by weight), and then stir evenly with an electric mixer.
7. Please use the specialized toner. The maximum amount of toner is 0.5% of the amount of glue.
8. Scraped back and forth with a scraper, and the glue is evenly applied on the bottom plate. According to the looseness of the material, single or double-sided glue can be applied;
9. Composite the plate, reciprocally shift the plate by hand and apply pressure to remove the air between the plates, so that the glue is fully filled, and there must be proper outflow of glue;
10. Align and press the plate up and down, the pressure should be evenly distributed, and the pressure method can be determined according to the actual situation (jack or clamp pressurization, etc.).
11. After standing under pressure, it can be solidified. It can be loosened after being cured at room temperature (25 °C) for 2-3 hours. After 24 hours, it can be put into the next process;
12. Waiting for solidify under pressure. Remove the pressure after being cured at room temperature (25 °C) for 2-3 hours. After 24 hours, it can proceed to the next process.
13. Please use the special cleaning agent to clean the tools before the glue is uncured.
Scrape off the residual glue when it is not cured